Modeling and experimental characterization of pearlitic rail steels subjected to large biaxial strains

Knut Andreas Meyer (Institutionen för industri- och materialvetenskap, Material- och beräkningsmekanik )
Gothenburg : Chalmers University of Technology, 2017.
[Licentiatavhandling]

Large shear strains develop in the near-surface region under the running band of railway rails. Rolling Contact Fatigue (RCF) cracks often initiate in this region, causing major problems for the railway industry. However, characterization of the constitutive and fatigue behavior of this region is difficult due to the large gradient of properties. In the present thesis, the deformed microstructure in this region is characterized. An axial-torsion test rig is used to predeform cylindrical low-cycle fatigue specimens in order to obtain material properties similar to those of the near-surface region in rails. These specimens are more suitable for further mechanical testing, compared to those resulting from many of the other predeformation methods described in the literature. The obtained material is compared to field samples in terms of the material hardness and microstructure. The microstructure is evaluated with both optical microscopy and scanning electron microscopy. This comparison shows that the predeformed material state closely resembles what is found in some used rails at a depth between 50 and 100 μm.

In order to describe the behavior of the material during the large shear deformations, a sound framework for finite strain metal plasticity is needed. Several options are available in the literature, but in this thesis two frameworks for hyperelasto-plasticity with kinematic hardening are investigated. It is shown that for appropriate choices of Helmholtz' free energy these frameworks are equivalent.

Furthermore, several material models formulated within this framework are evaluated in terms of their abilities to predict the mechanical response during the predeformation. Particular emphasis is put on the role of the kinematic hardening laws and how these influence the response during the biaxial loading. It is found that by combining different models from the literature, the predeformation process can be modeled accurately.

Nyckelord: Pearlitic steel, biaxial loading, kinematic hardening, axial-torsion, hyperelasto-plasticity



Den här publikationen ingår i följande styrkeområden:

Läs mer om Chalmers styrkeområden  

Denna post skapades 2017-09-13. Senast ändrad 2017-09-19.
CPL Pubid: 251873

 

Läs direkt!

Lokal fulltext (fritt tillgänglig)


Institutioner (Chalmers)

Institutionen för industri- och materialvetenskap, Material- och beräkningsmekanik

Ämnesområden

Materialvetenskap
Transport
Teknisk mekanik

Chalmers infrastruktur

C3SE/SNIC (Chalmers Centre for Computational Science and Engineering)

Relaterade publikationer

Inkluderade delarbeten:


A comparison of two frameworks for kinematic hardening in hyperelasto-plasticity


Examination

Datum: 2017-10-06
Tid: 13:15
Lokal: VDL, Chalmers Tvärgata 4C
Opponent: Professor Andreas Menzel, Institute of Mechanics, TU Dortmund University, Germany