Performance of Concrete Subjected to Severe Multiple Actions of Composite Salts Solution under Wet-Dry Cycles and Flexural Loading in Lab

Y. J. Chen ; J. M. Gao ; Luping Tang (Institutionen för bygg- och miljöteknik, Byggnadsteknologi) ; D. M. Shen
Journal of Wuhan University of Technology-Materials Science Edition (1000-2413). Vol. 32 (2017), 4, p. 830-837.
[Artikel, refereegranskad vetenskaplig]

Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity (E-rd values) were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis (GRA). The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction (XRD), mercury intrusion technique (MIP), and scanning electron microscopy (SEM). The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of E-rd values and the GEA. The analyses from micro-structures could give certain explanations to the change in E-rd values under different action regimes.

Nyckelord: concrete, wet-dry cycles, flexural loading, composite salts solution, grey relation analysis, Chloride Environment, Wetting Cycles, Sulfate Attack, Fly-Ash, Durability, Cement, Ingress, Water, Slag



Denna post skapades 2017-09-14.
CPL Pubid: 251891

 

Läs direkt!


Länk till annan sajt (kan kräva inloggning)


Institutioner (Chalmers)

Institutionen för bygg- och miljöteknik, Byggnadsteknologi (2005-2017)

Ämnesområden

Materialteknik

Chalmers infrastruktur